How to solve the problem of warping of stainless steel tensile parts?

By : Categories : Blog,Industry Comment: Comments Off on How to solve the problem of warping of stainless steel tensile parts?
  1. There is residual stress inside the stainless steel tensioned part, will it affect the tensioned part?

Because, if there is residual stress inside the stainless steel tensioned part, it will affect the strength, size, stability and service life of the tensioned part, and sometimes has a great impact. Therefore, at this point, we must pay attention and take some necessary measures to avoid and solve so as to avoid problems.

  1. How to solve the problem of warping of stainless steel tensile parts?

For stainless steel tensile parts, if there is a problem of warping, the solution is to anneal. If not, then use the right material. In order to prevent the sticking phenomenon, the brightness of the mold should be improved, and the above purpose can be achieved by using the appropriate stretching oil and the correct stretching coefficient.

3. Are the materials used in the tensile parts different and whether the elongation is different?

Tensile parts, when using materials, if the materials are different, the elongation will be different. Moreover, after stretching, the force on the material will also change, which is affected.

4. Can sandblasting be used to eliminate the internal stress of tensile parts?

Sandblasting for surface preparation cannot be used to relieve internal stresses in tensioned parts. From another point of view, in the sandblasting process, there will be some effects. Then, over time, it may reduce the internal stress of the tension member, so this is not correct.

Well, the above is the relevant content about “how to solve the problem of warping of stainless steel tensile parts?”, I hope the above content can help readers!